100% Original Factory Chlorine Bleach Resistance Fabric - 98% cotton 2% 3/1 S twill fire retardant and anti-static fabric 128*60/20A*16A for flame retardant protective clothing – Xiang Kuan
100% Original Factory Chlorine Bleach Resistance Fabric - 98% cotton 2% 3/1 S twill fire retardant and anti-static fabric 128*60/20A*16A for flame retardant protective clothing – Xiang Kuan Detail:
| Art No. | MBF9337Z |
| Composition | 98%Cotton2%SA |
| Yarn Count | 20A*16A |
| Density | 128*60 |
| Full Width | 57/58″ |
| Weave | 3/1 S twill |
| Weight | 280g/㎡ |
| Available Color | Red, Navy, orange etc. |
| Finish | Flame Retardant, Fire Retardant, Anti-static |
| Width Instruction | Edge-to-edge |
| Density Instruction | Greige Fabric Density |
| Delivery Port | Any port in China |
| Sample Swatches | Available |
| Packing | Rolls, fabrics length less than 30 yards are not acceptable. |
| Min order quantity | 5000 meter per color,5000 meter per order |
| Production Time | 30-35days |
| Supply Ability | 200,000 meters per month |
End Use: Flame retardant protective clothing for metallurgy, machinery, forestry, fire protection and other industries
Payment Terms: T/T in advance, LC at sight.
Shipment Terms: FOB, CRF and CIF, etc.
Fabric Inspection: This fabric can meet GB/T standard, ISO standard, JIS standard, US standard. All the fabrics will be 100 percent inspected before shipment according to American four point system standard.
| Fabric Composition | 98%Cotton 2% SA(10mm lattice conductive wire) | ||
| Weight | 280g/㎡ | ||
| Shrinkage | EN 25077-1994 | Warp | ±3% |
| EN ISO6330-2001 | Weft | ±3% | |
| Color fastness to washing（After 5 washes） | EN ISO 105 C06-1997 | 4 | |
| Color fastness to dry rubbing | EN ISO 105 X12 | 3 | |
| Color fastness to wet rubbing | EN ISO 105 X12 | 2-3 | |
| Tensile strength | ISO 13934-1-1999 | Warp(N) | 1306 |
| Weft(N) | 754 | ||
| Tear strength | ISO 13937-2000 | Warp(N) | 29.8 |
| Weft(N) | 26.5 | ||
| Flame retardant performance index | EN11611;EN11612;EN14116 | ||
| Fabric Composition | 98%Cotton 2% SA(10mm lattice conductive wire) | ||
| Weight | 280g/㎡ | ||
| Shrinkage | EN 25077-1994 | Warp | ±3% |
| EN ISO6330-2001 | Weft | ±3% | |
| Color fastness to washing（After 5 washes） | EN ISO 105 C06-1997 | 4 | |
| Color fastness to dry rubbing | EN ISO 105 X12 | 3 | |
| Color fastness to wet rubbing | EN ISO 105 X12 | 2-3 | |
| Tensile strength | ISO 13934-1-1999 | Warp(N) | 1306 |
| Weft(N) | 754 | ||
| Tear strength | ISO 13937-2000 | Warp(N) | 29.8 |
| Weft(N) | 26.5 | ||
| Flame retardant performance index | EN11611;EN11612;EN14116 | ||
About fire retardant fabric
Among all fire hazards, textiles getting burnt are more due to its widespread use. Majority of fire accidents are associated with the burning of textiles. Cellulosics that is commonly used in garments are comfortable, but are more prone to inflammability. The weight and weave of the fabrics also decides its inflammability. Heavy and tight woven fabrics burn slowly than loosely woven fabrics. Flammability is important, particularly for textiles. A retardant finish is given to fabrics to prevent it from getting burnt.
Product detail pictures:
Related Product Guide:
We believe that long term partnership is a result of high quality, value added service, rich experience and personal contact for 100% Original Factory Chlorine Bleach Resistance Fabric - 98% cotton 2% 3/1 S twill fire retardant and anti-static fabric 128*60/20A*16A for flame retardant protective clothing – Xiang Kuan, The product will supply to all over the world, such as: Indonesia, luzern, Lithuania, As an experienced manufacturer we also accept customized order and we could make it the same as your picture or sample specification. The main goal of our company is to live a satisfactory memory to all the customers, and establish a long term business relationship with buyers and users all over the world.
By Julie from Georgia - 2018.04.25 16:46
Reasonable price, good attitude of consultation, finally we achieve a win-win situation,a happy cooperation!
By Zoe from Portland - 2017.09.29 11:19